| dc.contributor.author | Syaila Muftiani, Aprilia | |
| dc.date.accessioned | 2024-08-14T02:19:35Z | |
| dc.date.available | 2024-08-14T02:19:35Z | |
| dc.date.issued | 2024-07-30 | |
| dc.identifier.uri | https://library.universitaspertamina.ac.id//xmlui/handle/123456789/12560 | |
| dc.description | Penambahan logam nikel oksida (NiO) sebagai impregnasi pada karbon aktif dari limbah batang mawar yang disintesis dengan metode pirolisis sebelum proses aktivasi dan metode hidrotermal setelah proses aktivasi dianalisis dalam penelitian ini. Proses aktivasi dilakukan dengan NaOH. Karakterisasi dari LBM-AC-NiO dianalisis menggunakan Fourier Transform Infra-Red (FTIR), Scanning Electron Microscopy – Energy Dispersive X-ray Spectroscopy (SEM-EDX), dan X-Ray Diffraction (XRD). Selain itu dilakukan uji elektrokimia berupa Cyclic Voltammetry (CV) dan Galvanostatic Charge-Discharge (GCD). Karakteridsdi Uji elektrokimia dilakukan menggunakan sistem 3 elektroda yaitu glassy carbon sebagai working electrode, Ag/AgCl sebagai reference electrode, platina wire sebagai counter electrode dan digunakanya 1M Na2SO¬4 sebagai elektrolit. Dari hasil karakterisasi yang dilakukan didapatkan bahwa terdapat ikatan C-O, C-H, C=C, O-H, dan NiO pada hasil FTIR, selain itu performa elektrokimia diuji pada Cyclic Voltammetry (CV) dan Galvanostatic Charge-Discharge (GCD) dengan hasil yang didapatkan menunjukkan bahwa adanya penambahan NiO ke dalam karbon aktif dapat meningkatkan nilai kapasitansi spesifik sebesar 361,91 F/g pada LBM-AC-NiO4. Berdasarkan hasil yang telah diperoleh, material Limbah Batang Mawar yang disintesis memiliki potensi untuk digunakan sebagai elektroda superkapasitor. | en_US |
| dc.description.abstract | The addition of nickel oxide (NiO) as an impregnation on activated carbon from rose stem waste, synthesized using the pyrolysis method before the activation process and the hydrothermal method after the activation process, is analyzed in this study. The activation process was carried out with NaOH. The characterization of LBM-AC-NiO was analyzed using Fourier Transform Infra-Red (FTIR), Scanning Electron Microscopy – Energy Dispersive X-ray Spectroscopy (SEM-EDX), and X-Ray Diffraction (XRD). Additionally, electrochemical tests were conducted in the form of Cyclic Voltammetry (CV) and Galvanostatic Charge-Discharge (GCD). Electrochemical tests were performed using a three-electrode system: glassy carbon as the working electrode, Ag/AgCl as the reference electrode, platinum wire as the counter electrode, and 1M Na2SO4 as the electrolyte. The characterization results showed the presence of C-O, C-H, C=C, O-H, and NiO bonds in the FTIR results. Furthermore, electrochemical performance was tested in Cyclic Voltammetry (CV) and Galvanostatic Charge-Discharge (GCD) with results indicating that the addition of NiO to activated carbon can increase the specific capacitance value to 361.91 F/g in LBM-AC-NiO4. Based on the results obtained, the synthesized rose stem waste material has the potential to be used as a supercapacitor electrode. | en_US |
| dc.publisher | Universitas Pertaminaa | en_US |
| dc.subject | Laporan Tugas Akhir | en_US |
| dc.title | Sintesis Dan Karakterisasi Karbon Aktif Berbasis Limbah Batang Mawar Dengan Impregnasi Nikel Oksida Sebagai Elektroda Superkapasitor. | en_US |